Originally Posted by johnnydmetal
I have used JB weld and it works fairly well but It requires a hotter flame then solder. With a tank having plating inside this would potentially leave a bare spot inside that could be damaged. The solder can be melted with minimal heat.
John
Umm, JB is a cold weld 2 part epoxy... no heat required, but a hair dryer does help a little.